uniaxial crystal grown with Czochralski method. It has good temperature stability and physical and mechanical properties, wide transparency and large birefringence, so it is also ideal for optical components such as fiber optical isolators and circulators, beam displaces and other polarizing optics, etc.| 0.633um | 1.30 um | 1.55 um | |||
| Refractive Indices: | no | 1. 9929 | 1.950 | 1.9447 | |
| ne | 2.2154 | 2.1554 | 2.1486 | ||
| Birefringence (Dn = ne - no) | 0.2225, | 0.2054 | 0.2039 | ||
| Walk-off Angle at 45º (r) | 6.04º at | 5.72º | 5.69º | ||
| Dimension tolerance | (W ± 0.1 mm) x (H ± 0.1 mm) xL( 0.05mm) |
| Transmitting wavefront distortion: | l/8 @ 633 nm |
| Clear aperture: | > 90% central area |
| Flatness: | l/8 @ 633 nm |
| Scratch/Dig code: | 10/5 to MIL-O-13830A |
| Parallelism: | better than 10 arc seconds |
| Perpendicularity: | 5 arc minutes |
| Angle tolerance: | Dq < ±0.5°, Df < ± 0.5° |
| AR coating: | R< 0.2% at 1550nm |
| Wedge Angle tolerance: | 0.1°(wedges) |