CLaser develops a new Q-Switch crystal Cr:ZnSe, for 1.4-2.2um application. It is very good for eye-safe laser systems.
Cr doping of commercial ZnSe was achieved through a thermal diffusion process employing CrSe powder as the dopant source. All samples exhibited the characteristic spectral features of Cr2+-doped II–VI materials with strong IR absorption bands between 1.4um and 2.2um and broad emission spectra from 2000 to 3400 nm. The room-temperature decay times were measured to be 5–6 μs for Cr:ZnSe. The emission lifetime of Cr2+ ions decreased by a factor of two for Cr concentrations of 2.6×1019 cm−3 for Cr:ZnSe.
 
Specifications:
|
Transmission range (μm)
|
0.5-22
|
|
Reflection index (1.65μm)
|
2.455
|
|
Index via temperature (10-6/℃)
|
61
|
|
Melting point (℃)
|
1520
|
|
Rigidity (kg/mm2)
|
112
|
|
Density g/cm3
|
5.27
|
|
Rupture modulus (MPa)
|
55.2
|
|
Rupture toughness (MPam1/2)
|
0.5
|
|
Yangs modulus (GPa)
|
67.5
|
CLaser can supply Cr:ZnSe from 3mm to 10mm in diameter, Transmission from 20-90%. AR coating is available for your request.
|